Competing damage modes in all-ceramic crowns: Fatigue and lifetime

Yu Zhang, Brian Lawn

Research output: Contribution to journalArticle

Abstract

A study is made of fracture from cyclic loading of WC spheres on the surfaces of brittle layers on compliant substrates, as representative of repetitive occlusal contact on dental crowns. Several damage modes-radial cracks at both top surface and cementation interface, and classical cone cracks as well as deep penetrating cone cracks from the top surface-have been identified and analyzed. The most dangerous fractures are radial cracks that initiate from either the top or bottom surfaces of the brittle layers and spread laterally to failure. In fatigue, these cracks are driven by chemical forces associated with the intrusion of water into the crack. Also dangerous are deep penetrating cone cracks which, unlike their classical cone crack counterparts, are mechanically driven by hydraulic pumping and can evolve rapidly with cyclic loading, threatening the lifetime of a dental crown veneer.

Original languageEnglish (US)
Pages (from-to)697-700
Number of pages4
JournalKey Engineering Materials
Volume284-286
DOIs
StatePublished - 2005

Keywords

  • Ceramic crowns
  • Damage modes
  • Fatigue
  • Layer structures
  • Lifetime

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Competing damage modes in all-ceramic crowns: Fatigue and lifetime'. Together they form a unique fingerprint.

  • Cite this